Zhongfa PA66 ST-06
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Yuyao Zhongfa Engineering Plastics Co. Ltd. |
| Trademark: | Zhongfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w053vW_Zhongfa-PA66-ST-06.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zhongfa PA66 ST-06 is a polyamide 66 (nylon 66) material,. This product is available in the Asia-Pacific region and is processed by injection molding. The main characteristics of Zhongfa PA66 ST-06 are: impact resistance. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 11 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 1500 | MPa | ASTM D790 |
| Flexural Strength | 81.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Notched Izod Impact, ASTM D256: 12 kJ/m² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 90.0 | °C | |
| Drying Time | 6.0 - 8.0 | hr | |
| Processing (Melt) Temp | 235 - 265 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 60.0 - 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 GI-1220 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Andur M-22 (94% 1,4BD, 6% TMP) | Anderson Development Company | PUR-Ester/MDI | Andur |
| FERREX® GPP40CC47HB | Ferro Corporation | PP Homopolymer | FERREX® |
| PLUSTEK PA840G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| LNP™ THERMOCOMP™ PF006U compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |