FORMOCON® FM025
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | FORMOCON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vzaZni_FORMOCON-FM025.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characteristics: High viscosity, extrusion, minimal mould. Application: Extruded rods and sheets, other extrusion parts. Also known as FORMOSACON |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.8 to 2.2 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 69%RH) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 59.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 75 | % | ASTM D638 |
| Flexural Modulus | 2550 | MPa | ASTM D790 |
| Flexural Strength | 93.2 | MPa | ASTM D790 |
| Compressive Strength | ASTM D695 | ||
| 1% Strain | 31.4 | MPa | |
| 10% Strain | 108 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 158 | °C | |
| 1.8 MPa, Unannealed | 110 | °C | |
| Vicat Softening Temperature | 162 | °C | ASTM D1525 |
| Melting Temperature | 165 | °C | DSC |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 1 | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity 2(23°C) | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 24 | kV/mm | ASTM D149 |
| Dielectric Constant | IEC 60250 | ||
| 50 Hz | 3.80 | ||
| 1 kHz | 3.80 | ||
| 1 MHz | 3.80 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 50%RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GBF 3310 HI H LS | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Titalon® 1100CF | Titan Plastics Compounds Co., Ltd. | Nylon 6 | Titalon® |
| Xuchuan XCW-6010EB | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Andur 6500 DP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Fainplast PVC GS 58 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |