Toyolac® 560-X17
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vzV2nW_Toyolac-560-X17.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® 560-X17 is an Acrylonitrile Butadiene Styrene (ABS) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 118 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 51.0 | MPa | ASTM D638 |
| 23°C | 55.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 17 | % | ASTM D638 |
| Break, 23°C | 21 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2880 | MPa | ASTM D790 |
| 23°C | 2960 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 84.0 | MPa | ASTM D790 |
| 23°C | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 39 | J/m | |
| -30°C, 12.7 mm | 29 | J/m | |
| 0°C, 3.20 mm | 49 | J/m | |
| 0°C, 12.7 mm | 39 | J/m | |
| 23°C, 3.20 mm | 69 | J/m | |
| 23°C, 12.7 mm | 69 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 83.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C | |
| CLTE - Flow | 6.4E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® A3 GF 25 1 L black (4672) | AKRO-PLASTIC GmbH | Nylon 66+PP | AKROMID® |
| Kingfa PA6-MG45 | Kingfa | Nylon 6 | Kingfa |
| O'Tech OM 6539 | O'Tech Corporation | PVC, Unspecified | O'Tech |
| Sumiliteresin® ECP-354 | SBHPP | Epoxy | Sumiliteresin® |
| Sarlink® TPE ML-1140N NAT (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |