LEXAN™ 9915A resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vy0RfF_LEXAN-9915A-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LEXAN 9915A Polycarbonate (PC) resin is an un-filled, extrusion or injection moldable grade; non-chlorinated, non-brominated flame retardant systems with UL-90 V0 rating @1.5mm. It is UV stabilized & available in transparent & tinted color options. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.20 | g/cm³ | |
| -- | 1.07 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1 | 0.60 to 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2320 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 64.0 | MPa | |
| Break | 62.0 | MPa | |
| Tensile Elongation 4 | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 110 | % | |
| Flexural Modulus 5(50.0 mm Span) | 2330 | MPa | ASTM D790 |
| Flexural Strength 6(Yield, 50.0 mm Span) | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 120 | J/m | |
| 23°C | 800 | J/m | |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 75.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 142 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | |
| Vicat Softening Temperature | 146 | °C | ISO 306/B120 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 95°C | 6.8E-5 | cm/cm/°C | |
| Transverse : -40 to 95°C | 6.8E-5 | cm/cm/°C | |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 260 to 282 | °C | |
| Middle Temperature | 271 to 293 | °C | |
| Front Temperature | 282 to 304 | °C | |
| Nozzle Temperature | 277 to 299 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 2773 | Teknor Apex Company | TPE | Sarlink® TPV |
| Teldene® H03ML | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |
| Axiall PVC 9113J Clear 13 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| ICORENE® N2807 | ICO Polymers EMEA, A Division of A. Schulman | HDPE | ICORENE® |
| POLYFORT® FPP 10 GFC | A. Schulman Europe | PP Homopolymer | POLYFORT® |