AFFINITY* PF 1140G Polyolefin Plastomer (POP) is produced via INSITE* Technology. It is an ethylene alpha-olefin resin designed to be used in a variety of demanding applications including form-fill-seal packaging and fresh produce bags. This resin has excellent compatibility with other polyolefins, allowing efficient blending and coextrusion. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.897 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.6 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy (51 µm) | 8.18 | J | Internal method |
| Film Puncture Force (51 µm) | 83.6 | N | Internal method |
| Film Puncture Resistance (51 µm) | 20.3 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 72.8 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 73.2 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 5.79 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 6.34 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 50.3 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 39.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 690 | % | ASTM D882 |
| TD : Fracture, 51 µm | 700 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | > 850 | g | ASTM D1709B |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 51 µm | 470 | g | ASTM D1922 |
| TD : 51 µm | 620 | g | ASTM D1922 |
| Seal Initiation Temperature 2(51 µm) | 81.1 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 76.7 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 96.1 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°, 50.8 µm) | 134 | ASTM D2457 | |
| Clarity (50.8 µm) | 70.0 | ASTM D1746 | |
| Haze (50.8 µm) | 1.3 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 209 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：单跨双混合 模具间隙：70 密尔 (1.8 mm) 熔体温度：408°F (209°C) 输出：模具周长的 6 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：50 rpm 冷冻线高度：25 英寸 (635 mm) |
| Note Message | |
|---|---|
| 1 . | Modified rectangular test piece. |
| 2 . | Achieve a temperature of 2 psig (8.8 N/25.4mm) heat seal strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed 10 inches/min (250 mm/s). |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stirol UPM-424 (extra) | JSC CONCERN STIROL | PS (HIPS) | Stirol |
| SWANCOR Epoxy 901 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| VITAMIDE® AR36BK9022 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Boda BDF-KK2801 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Formolene® 4143T | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |