LIM™ 6050
| Category: | Silicone Rubber, LSR , Silicone Rubber, LSR |
| Manufacturer: | Momentive Performance Materials Inc. |
| Trademark: | LIM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vxhaXw_LIM-6050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LIM6050 liquid silicone rubber is a 2-component product formulated for use in liquid injection molding to high performance elastomeric parts. It is clear, but easily pigmentable with Momentive masterbatch colors. The combination of excellent tear strength and very high tensile strength makes this product suitable for a wide variety of applications. Mechanical parts such as connector inserts, seals, flexible mounts, and valve parts can be made readily from LIM6050 liquid silicone rubber. Key Features and Benefits
Potential Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Bayshore Resilience | |||
| -- 1 | 58 | % | |
| -- 2 | 60 | % |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 3 | Clear/Transparent | ||
| -- 4 | Clear/Transparent | ||
| Density | |||
| -- 5 | 1.12 | g/cm³ | |
| -- 6 | 1.12 | g/cm³ |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness | |||
| Shore A 7 | 50 | ||
| Shore A 8 | 53 | ||
| Tensile Modulus | |||
| 100% Secant 9 | 2.10 | MPa | |
| 100% Secant 10 | 2.20 | MPa | |
| Tensile Strength | |||
| -- 11 | 8.60 | MPa | |
| -- 12 | 9.00 | MPa | |
| Tensile Elongation at Break | |||
| -- 13 | 530 | % | |
| -- 14 | 580 | % | |
| Compression Set | |||
| 177°C, 22.0 hr 15 | 25 | % | |
| 177°C, 22.0 hr 16 | 35 | % | |
| Tear Strength | |||
| -- 17 | 43.9 | kN/m | |
| -- 18 | 43.9 | kN/m | |
| Electric Strength 19 | 20 | kV/mm | |
| Relative Permittivity 20(1 kHz) | 3.12 | ||
| Volume Resistivity 21 | 6.1E+14 | ohms·cm | |
| Dissipation Factor 22(1 kHz) | 1.0E-4 |
| Note Message | |
|---|---|
| 1 . | Postbaked 1 hr @ 204°C (400°F) |
| 2 . | As Molded 30 sec @ 177°C (350°F) |
| 3 . | Part B |
| 4 . | Part A |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | As Molded 30 sec @ 177°C (350°F) |
| 8 . | Postbaked 1 hr @ 204°C (400°F) |
| 9 . | As Molded 30 sec @ 177°C (350°F) |
| 10 . | Postbaked 1 hr @ 204°C (400°F) |
| 11 . | As Molded 30 sec @ 177°C (350°F) |
| 12 . | Postbaked 1 hr @ 204°C (400°F) |
| 13 . | Postbaked 1 hr @ 204°C (400°F) |
| 14 . | As Molded 30 sec @ 177°C (350°F) |
| 15 . | Postbaked 1 hr @ 204°C (400°F) |
| 16 . | As Molded 30 sec @ 177°C (350°F) |
| 17 . | Postbaked 1 hr @ 204°C (400°F) |
| 18 . | As Molded 30 sec @ 177°C (350°F) |
| 19 . | As Molded 30 sec @ 177°C (350°F) |
| 20 . | As Molded 30 sec @ 177°C (350°F) |
| 21 . | As Molded 30 sec @ 177°C (350°F) |
| 22 . | As Molded 30 sec @ 177°C (350°F) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 2012 | Nycoa (Nylon Corporation of America) | Nylon+TPE | NYCOA Polyamide |
| DAI-EL™ G-7211 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Karina WHITE PVC COMPOUND 800-10/93-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Rotuba CAP CP808 (17% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |
| Sylvin 9772-75 Brown 7211 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |