LOFEX® A4111
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | LOFEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vxHegV_LOFEX-A4111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LOFEX ® A4111 Polyester film is optically clear and both sides corona treated with excellent properties by tensile strength , proper elongation and the thermal contraction rate. It can use by release film because it has excellent run, easy treatment by suitable product. Also, it is a product that thickness control is possible according to customer needs. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Tension | |||
| 50.0 µm | 52 | mN/m | |
| 75.0 µm | 52 | mN/m | |
| 100.0 µm | 52 | mN/m | |
| 125.0 µm | 52 | mN/m |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| F5 | ASTM D882 | ||
| MD : 50.0 µm | 113 | MPa | |
| MD : 75.0 µm | 113 | MPa | |
| MD : 100.0 µm | 113 | MPa | |
| MD : 125.0 µm | 113 | MPa | |
| TD : 50.0 µm | 113 | MPa | |
| TD : 75.0 µm | 113 | MPa | |
| TD : 100.0 µm | 113 | MPa | |
| TD : 125.0 µm | 113 | MPa |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Shrinkage | Internal Method | ||
| MD, 30 min : 125.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 50.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 75.0 µm | 1.0 | % | |
| MD, 30 min : 150°C, 100.0 µm | 1.0 | % | |
| TD, 30 min : 150°C, 50.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 75.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 100.0 µm | 0.50 | % | |
| TD, 30 min : 150°C, 125.0 µm | 0.50 | % | |
| Surface Treatment | Both sides (Corona) |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.30 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 196 | MPa | |
| MD : Yield, 75 µm | 196 | MPa | |
| MD : Yield, 100 µm | 196 | MPa | |
| MD : Yield, 130 µm | 186 | MPa | |
| TD : Yield, 50 µm | 235 | MPa | |
| TD : Yield, 75 µm | 216 | MPa | |
| TD : Yield, 100 µm | 216 | MPa | |
| TD : Yield, 130 µm | 206 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 170 | % | |
| MD : Break, 75 µm | 170 | % | |
| MD : Break, 100 µm | 170 | % | |
| MD : Break, 130 µm | 170 | % | |
| TD : Break, 50 µm | 120 | % | |
| TD : Break, 75 µm | 120 | % | |
| TD : Break, 100 µm | 120 | % | |
| TD : Break, 130 µm | 120 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 60°, 50.0 µm | 160 | ||
| 60°, 75.0 µm | 160 | ||
| 60°, 100 µm | 160 | ||
| 60°, 125 µm | 160 | ||
| Transmittance | ASTM D1003 | ||
| 50.0 µm | 88.0 | % | |
| 75.0 µm | 88.0 | % | |
| 100 µm | 88.0 | % | |
| 125 µm | 88.0 | % | |
| Haze | ASTM D1003 | ||
| 50.0 µm | 2.0 | % | |
| 75.0 µm | 2.5 | % | |
| 100 µm | 3.4 | % | |
| 125 µm | 3.5 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESNO P40 TL3 | Arkema | Nylon 11 | Rilsan® |
| UBE Nylon 5033 TX7 | UBE Engineering Plastics, S.A. | Nylon 66/6 | UBE Nylon |
| Celcon® MC90 | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Generic MDPE | Generic | MDPE | Generic |
| EPO-TEK® T6065 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |