INEOS LDPE 24F760
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vwYo1M_INEOS-LDPE-24F760.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
24F760 is an autoclave LDPE grade developed intended for lamination film and general packaging film. 24F760 is developed to give film with good optical properties and low gel level for medium duty film. Applications 24F760 is intended for applications such as
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm | 27.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm | 24.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 40 µm | 250 | % | ISO 527-3 |
| TD : Break, 40 µm | 550 | % | ISO 527-3 |
| Dart Drop Impact (40 µm) | 120 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm | 4.0 | N | ISO 6383-2 |
| TD : 40 µm | 2.0 | N | ISO 6383-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (40.0 µm) | 80 | ASTM D2457 | |
| Haze (40.0 µm) | 10 | % | ASTM D1003 |
| Additional Information |
|---|
| Tensile Modulus, ASTM D882-A, MD, 40µ: 230 MPaTensile Modulus, ASTM D882-A, TD, 40µ: 260 MPaCoefficient of Friction, ISO 8295, dynamic, 40µ: 0.8The value listed as Elmendorf Tear Strength ISO 6383-2, was tested in accordance with ISO 8483/2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP2B40 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| Mirakutoran® TPU E380PKOO | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| ELASTOSIL® E 91 | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| LIHAN® A9705NP | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| LNP™ STAT-KON™ DD0001 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |