CEFOR™ 1220P
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | CEFOR™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vwVUee_CEFOR-1220P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CEFOR 1220P is a butene Linear Low Density Polyethylene for general blown film extrusion film applications. Main Characteristics:
Complies with:
Additive:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Film Puncture Resistance (38 µm) | 5.00 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 38 µm | 150 | MPa | ASTM D882 |
| 2% secant, TD : 38 µm | 145 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 10.0 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 33.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 25.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 950 | % | ASTM D882 |
| TD : Fracture, 38 µm | 1100 | % | ASTM D882 |
| Dart Drop Impact (38 µm) | 140 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 220 | g | ASTM D1922 |
| TD : 38 µm | 330 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.7 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 116 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.1 µm) | 53 | ASTM D2457 | |
| Haze (38.1 µm) | 13 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Fabrication Conditions For Blown Film: Melt Temperature: 428°F (206°C) Die Gap: 70mil (1.8mm) Output: 120 lb/hr (54kg/fr) Blow-Up Ratio: 2.5:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® PM-8180 | Sumitomo Bakelite Co., Ltd. | Phenolic | Sumikon® |
| Sumiflex® QE QE533AEE | Mitsubishi Chemical Corporation | TES | Sumiflex® QE |
| VITAMIDE® BR3X | A. Schulman Europe | Nylon 6 | VITAMIDE® |
| Xuchuan XCW-90BA-6B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| KPOL-LLDPE LLD K-I 35/926 | KPOL Chem Co. | LLDPE | KPOL-LLDPE |