Synthos EPS® 1325F/PL
| Category: | PS (EPS) , Expanded Polystyrene |
| Manufacturer: | Synthos S.A. |
| Trademark: | Synthos EPS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vvebsL_Synthos-EPS-1325F-PL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Synthos EPS® F /PL type 0308F, 0513F, 0816F and 1325F is self-extinguishing expandable polystyrene EPS with high content of pentane. The materials are formed by spherical polystyrene particles that contain a flame retardant system (content of HBCD < 0,5%) and a hydrocarbon blowing agent. Their surface is treated against gluing during processing and the formation of electrostatic charge. Due to the content of halogenated flame retardant and the residual blowing agent, the product is unsuitable for objects intended for direct contact with food. Synthos EPS® 1325F/PL (Owipian FS 1325) is mainly used for production of high volume blocks with low-density; of cutted boards and profiles from the blocks for a thermal insulation e.g. building objects. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | Internal Method | ||
| -- 1 | < 0.02 | g/cm³ | |
| -- 2 | 0.02 to 0.04 | g/cm³ | |
| Moisture Content | < 10000 | ppm | Internal Method |
| Particle Size - >95% between | 1.25 to 2.50 | mm | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Reaction to Fire | |||
| -- | B1 | DIN 4102 | |
| -- | Class E | EN 13501-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blowing Agent | < 7.0 | wt% | Internal Method |
| Note Message | |
|---|---|
| 1 . | The laboratory tests of expanded beads bulk density are made according to Polish Standard PN-90/C-89298 using the following expansion times: 0308 and 0513: 12 min., 0816: 10 min., 1325: 6 min. |
| 2 . | The typical bulk density indicates values obtained during single-step pre-foaming on continuous pre-foaming devicesLower values of bulk density can be achieved only after multiple pre-expansion. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TO 137 | Mitsubishi Chemical Performance Polymers, Inc. | SBS | tefabloc® |
| Veroplas SKG20 | PlastxWorld Inc. | ABS | Veroplas |
| Bergamid™ A70 G15 HW TM-Z | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Delrin® PC690 NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Generic Nylon 46 - Glass Fiber | Generic | Nylon 46 | Generic |