ProvaMed® TPE 1080
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | ACTEGA GmbH |
| Trademark: | ProvaMed® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vvFzRN_ProvaMed-TPE-1080.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ProvaMed® TPE 1080 is a Thermoplastic Elastomer (TPE) material. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of ProvaMed® TPE 1080 are:
Typical application of ProvaMed® TPE 1080: Medical/Healthcare |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/5.0 kg | 4.0 | g/10 min | |
| 230°C/2.16 kg | 6.0 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 5 sec | 80 | ||
| Shore D, 5 sec | 26 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 3.90 | MPa | DIN 53504 |
| Tensile Stress (Yield) | 11.0 | MPa | DIN 53504 |
| Tensile Elongation (Break) | 690 | % | DIN 53504 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 21 | % | |
| 70°C, 22 hr | 78 | % | |
| 100°C, 22 hr | 93 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 1 | -13.0 | °C | DSC |
| Melting Temperature (DSC) 2 | 163 | °C | DSC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 20.0 to 30.0 | °C | |
| Rear Temperature | 140 to 230 | °C | |
| Middle Temperature | 140 to 230 | °C | |
| Front Temperature | 140 to 230 | °C | |
| Nozzle Temperature | 190 to 230 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Heating rate 10 K/minMelting peak from second heating cycle |
| 2 . | Heating rate 10 K/minMelting peak from second heating cycle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1700 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Shin-Etsu Elastomer KE-5530U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| SI-LINK™ DFDB-5410 BK | The Dow Chemical Company | PE, Unspecified | SI-LINK™ |
| Wellamid® NY1820-BK1(PTFE) | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| CYCOLAC™ DL200H resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |