Order Products : sales@su-jiao.com
SABIC® PP 86MF10
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vtxH8L_SABIC-PP-86MF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A grade which is characterized by an optimum combination of stiffness, impact resistance and flow. This grade is also available in a UV-stabilized version. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 4.7 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 18 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 2.00mm | 25.0 | MPa | ISO 527-2/50 |
| Fracture, 2.00mm | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 2.00 mm) | 500 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 | |
| Notched Izod Impact | ISO 180/A | ||
| -40°C | 4.5 | kJ/m² | ISO 180/A |
| -20°C | 6.8 | kJ/m² | ISO 180/A |
| 0°C | 14 | kJ/m² | ISO 180/A |
| 23°C | No Break | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 140 | °C | ISO 306/A50 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Mold Shrinkage, SABIC Method: 1.6% |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2602X1 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TOTAL Polypropylene PPC 7712 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Elastron® V P.V101.A90.B | Elastron USA, Inc. | TPV | Elastron® V |
| Plaslube® PA4/6 CF30 TL15 | Techmer Engineered Solutions | Nylon 46 | Plaslube® |
| Zytel® FE270088 BK099 | DuPont Performance Polymers | Nylon 66 | Zytel® |