ACLAR® 33C (2 mil)
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | ACLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vtrmXg_ACLAR-33C-2-mil-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Aclar 33C is a copolymer film consisting primarily of chlorotrifluoroethylene (CTFE). It has excellent moisture barrier and chemical resistance. 33C is used for military and industrial packaging applications as a monolayer film or as a barrier layer in laminate structures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.12 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 51 µm | 1470 | MPa | ASTM D882 |
| TD : 51 µm | 1410 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 57.2 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 31.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 51 µm | 160 | % | ASTM D882 |
| TD : Yield, 51 µm | 150 | % | ASTM D882 |
| Water Vapor Transmission Rate (51 µm, 38°C, 100% RH) | 0.14 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 206 | °C | ASTM D3418 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (0.0508 mm) | 100 | % | ASTM D2863 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.8 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield, No Standard: 9.3 m²/kgTear Strength, ASTM D1004, Graves MD: 400 to 500 g/milTear Strength, ASTM D1004, Graves TD: 375 to 475 g/milCrystalline Melting Point, ASTM D4591: 206 °CDimensional Stability, ASTM D1204, MD: |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 578N | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PP |
| SEPTON™ 8007 | Kuraray Co., Ltd. | SEBS | SEPTON™ |
| ADMER™ AT1113A | Mitsui Chemicals America, Inc. | PE, Unspecified | ADMER™ |
| GAPEX® RPP20EB76NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| SABIC® COHERE™ 8102L | Saudi Basic Industries Corporation (SABIC) | POP | SABIC® COHERE™ |