Propafilm™ OLS65
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vsozd5_Propafilm-OLS65.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Speed Overwraping Film with Shrink Tightening Properties Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with heat sealable polyolefinic copolymers. OLS65/80/100 are suitable for high speed overwrapping and horizontal form-fill applications where exceptional pack appearance and wrap tightness are required. The wide sealing range and enchanced machine performance make OLS films particularly suited to demanding magnectic and optical media, confectionery and tea applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 80°C, 1 min | 3.7 | % | |
| Flow : 120°C, 1 min | 7.0 | % | |
| Across Flow : 80°C, 1 min | 3.5 | % | |
| Across Flow : 120°C, 1 min | 11 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.30 | ||
| vs. Itself - Static, Outside/Outside | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD | 3000 | MPa | |
| 1% Secant, TD | 3600 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 170 | MPa | |
| TD : Yield | 210 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 120 | % | |
| TD : Break | 80 | % | |
| Seal Strength 4 | 0.19 | N/mm | Internal Method |
| Seal Initiation Temperature 5 | 110 to 141 | °C | Internal Method |
| Oxygen Permeability (23°C, 0% RH) | 56 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate | ASTM F1770 | ||
| 23°C, 85% RH | 1.4 | g/m²/24 hr | |
| 38°C, 90% RH | 7.6 | g/m²/24 hr | |
| Film Gauge | 65.0 | Internal Method | |
| Yield | 68.6 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | 130 | ASTM D2457 | |
| Haze 6 | 1.3 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| 4 . | 225°F; 1sec; 15lb/in² |
| 5 . | 2secs; 15lb/in² |
| 6 . | Wide angle, 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 6504 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Viton® VTR-9180 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| INEOS PP H38G-02 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| COSMOPLENE® AZ191 | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Copolymer | COSMOPLENE® |
| LNP™ STAT-KON™ RD000I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |