Halene H B6401
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vrKcdk_Halene-H-B6401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
B6401 is a HDPE Blow Molding Grade produced by the Mitsui CX Process. This resin is particularly recommended for up to 20-liter containers for Lubricants and Edible oils. B6401 combines exceptional processability with high rigidity, excellent mechanical properties and impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.964 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield, Compression Molded) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Compression Molded) | > 1000 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1300 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 350 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 4 |
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 165 | °C | |
| Cylinder Zone 4 Temp. | 175 | °C | |
| Die Temperature | 180 - 185 | °C |
| Extrusion instructions |
|---|
| Parison Temperature: 185-190°CCooling Water for Mold: 20-25°C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8333G HI | BASF Corporation | Nylon 6 | Ultramid® |
| Andur 80-5AP/Curene® 280 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Andur AL 80-5 AP/Curene® 111 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Karina COMP. PVC YELLOW. -E 600-DA-02/381-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUND 818-10/121-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |