Order Products : sales@su-jiao.com
CYCOLAC™ INP581 resin
| Category: | ABS+SAN , Acrylonitrile Butadiene Styrene + SAN |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vqu4sS_CYCOLAC-INP581-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow, low molecular weight SAN. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direct weather exposure. Provides excellent flow for demanding injection molding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 38 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 98 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4090 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 48.8 | MPa | |
| Break | 60.2 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 1.5 | % | |
| Break | 1.9 | % | |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3440 | MPa | ASTM D790 |
| -- 5 | 3520 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 36.3 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 66.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -30°C | 12 | J/m | ASTM D256 |
| 23°C | 23 | J/m | ASTM D256 |
| -30°C 7 | 1.4 | kJ/m² | ISO 180/1A |
| 23°C 8 | 1.6 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 97.6 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 86.9 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 82.9 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/B50 |
| -- | 105 | °C | ISO 306/B120 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 1.6 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAFORM® 9 A GF 25 | A. Schulman Europe | Acetal (POM) Copolymer | SCHULAFORM® |
| Novamid® 1033NY | DSM Engineering Plastics | Nylon 6 | Novamid® |
| Grivory® GV-6H EF black 9915 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Karina GRAY PVC COMPOUND 828-18/447-AY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Vyncolit® A2710 | SBHPP | Phenolic | Vyncolit® |