HANWHA EVA 1628

Category:	EVA , Ethylene Vinyl Acetate Copolymer
Manufacturer:	Hanwha Chemical
Trademark:	HANWHA EVA
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vprEvd_HANWHA-EVA-1628.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
HANWHA EVA 1628 designed for extrusion process is manufactured with exhaustive inspection to be used as a solar cell encapsulant. Specially, EVA 1628 is consistent with customer demands to meet a quality of solar modules. Optimized processablity for producing EVA sheet in a extrusion equipment. Improved yellowing resistance and cross-linking efficiency compared with conventional grades. Good compatibility with additives and optical property (transmittance and haze) to ensure solar cell efficiency.

Message

HANWHA EVA 1628 designed for extrusion process is manufactured with exhaustive inspection to be used as a solar cell encapsulant. Specially, EVA 1628 is consistent with customer demands to meet a quality of solar modules.

Optimized processablity for producing EVA sheet in a extrusion equipment.

Improved yellowing resistance and cross-linking efficiency compared with conventional grades.

Good compatibility with additives and optical property (transmittance and haze) to ensure solar cell efficiency.

General Information
Features	Copolymer Good Processability
Uses	Solar Panels
Agency Ratings	FDA 21 CFR 177.1350(a)(1)
Forms	Pellets
Processing Method	Extrusion Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Density	0.949	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	18	g/10 min	ASTM D1238
Vinyl Acetate Content	28.0	wt%	Internal Method

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	13.7	MPa	ASTM D638
Tensile Elongation (Break)	920	%	ASTM D638

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746
Vicat Softening Temperature	46.0	°C	ASTM D1525
Melting Temperature	71.0	°C	ASTM D3417

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3782	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
NEOPLAST 155 M/E	Zylog Plastalloys	TPE	NEOPLAST
EvoSource™ ABS 4136	MBA Polymers	ABS	EvoSource™
POCAN® BF 4409 000000	LANXESS Corporation	PBT	POCAN®
Hostacom X M2 V05 C11323	LyondellBasell Industries	PP Copolymer	Hostacom