NORYL™ SE1GFN2 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vpUvbW_NORYLSE1GFN2resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL SE1GFN2 is a 20% glass reinforced, injection moldable modified polyphenylene ether resin. Designed for improved dimensional stability and good flow , this resin also uses non-chlorinated, non-brominated FR additives to achieve a V1 UL94 rating at 1.5 mm and UL94 5VA rating @ 2.0 mm. NORYL SE1GFN2 has a GWIT of 800C @ 1.00 mm according to IEC 60695-2-13. NORYL SE1GFN2 may be an excellent material candidate for electrical or electronic applications requiring good rheological properties, heat resistance, hydrolysis resistance, low density and thin wall flame resistance. SE1GFN2 is halogen free according to VDE/DIN 472 part 815. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/10.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.20 - 0.40 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.22 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.070 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 125 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 80.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 4500 | MPa | ISO 178 |
| Flexural Stress | 125 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 65.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength 4 | ISO 180/1U | ||
| -30°C | 25 | kJ/m² | ISO 180/1U |
| 23°C | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 135 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 130 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 140 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | IEC 60695-10-2 | |
| 135°C 6 | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 5.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 23 to 80°C | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.28 | W/m/K | ISO 8302 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 30 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 3.00 | IEC 60250 | |
| 60 Hz | 3.00 | IEC 60250 | |
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 4.0E-3 | IEC 60250 | |
| 60 Hz | 4.0E-3 | IEC 60250 | |
| 1 MHz | 2.0E-3 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | UL 94 | |
| 6.00 mm | V-0 | UL 94 | |
| 2.00 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | IEC 60695-2-13 |
| 2.00 mm | 800 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 240 - 260 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 260 - 280 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 120*10*4 mm |
| 6 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HI5206R | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| UBE Nylon 1022 MT2 | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |
| KRATON® D1184 A | Kraton Polymers LLC | SBS | KRATON® |
| Lion Idemitsu Composites PPS C-200SC | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| Sylvin 6240-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |