Order Products : sales@su-jiao.com
Marlex® 7104
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vowELv_Marlex-7104.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Marlex® 7104 is a Linear Low Density Polyethylene material. It is available in Latin America or North America for coextrusion or sheet extrusion. Important attributes of Marlex® 7104 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | |||
| 10% Igepal, Compression Molded, F50 | > 2000 | hr | ASTM D1693B |
| 100% Igepal, Compression Molded, F50 | > 2000 | hr | ASTM D1693C |
| SP-NCTL | > 1.4 | month | ASTM D5397 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (200°C) | > 100 | min | ASTM D3895 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 51 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 11.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 700 | % | ASTM D638 |
| Flexural Modulus - Tangent 3(Compression Molded) | 410 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Compression Molded) | 51.0 | °C | ASTM D648 |
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoTek KM6085 | KMI Group Inc. | PBT | PrimoTek |
| Clariant Nylon 6/6 6608G43-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Clyrell RC249R | LyondellBasell Industries | PP Random Copolymer | Clyrell |
| GAPEX® FPP30GQ04 BLACK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Hostacom XBR 169 G G31463 | LyondellBasell Industries | PP Copolymer | Hostacom |