LNP VERTON NV008E is a compound based on PC+ABS resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding. Structural. Also known as: LNP* VERTON* Compound PCA-F-7008 EM Product reorder name: NV008E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.49 | g/cm³ | ASTM D792 |
| -- | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Across Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.27 | % | ISO 294-4 |
| Flow : 24 hr | 0.050 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 20300 | MPa | ASTM D638 |
| -- | 12400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 147 | MPa | ASTM D638 |
| Yield | 156 | MPa | ISO 527-2 |
| Break | 147 | MPa | ASTM D638 |
| Break | 156 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.4 | % | ASTM D638 |
| Yield | 1.3 | % | ISO 527-2 |
| Break | 1.4 | % | ASTM D638 |
| Break | 1.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11000 | MPa | ASTM D790 |
| -- | 11700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 214 | MPa | ASTM D790 |
| -- | 224 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 320 | J/m | ASTM D256 |
| 23°C | 300 | J/m | ASTM D256 |
| -40°C 2 | 34 | kJ/m² | ISO 180/1A |
| 23°C 3 | 28 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 740 | J/m | ASTM D4812 |
| 23°C 4 | 50 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 14.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 131 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 2.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.3E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 282 to 293 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 60.0 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP340M | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Ferro PP TPP20AE63BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| HiFill® PVDF CF15-M BK | Techmer Engineered Solutions | PVDF | HiFill® |
| HiFill® PP GF/M30 CC BK | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| PHOENIX™ 11401 | Phon Tech Industrial Company | SBC | PHOENIX™ |