MARPOL® HDM 545
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Marco Polo International, Inc. |
| Trademark: | MARPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vomm5s_MARPOL-HDM-545.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Recommended Applications: Dairy containers, margarine containers, butter tubs and promotional drink cups. |
| General Information | |
|---|---|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.946 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.62 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 45 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.3 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 979 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | 24 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 63.9 | °C | ASTM D648 |
| Vicat Softening Temperature | 121 | °C | ASTM D1525 |
| Peak Melting Temperature | 126 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-80A-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Sumikon® EME-7320AR | Sumitomo Bakelite Co., Ltd. | Epoxy | Sumikon® |
| Zytel® HTN 51G45HSL NC010 | DuPont Performance Polymers | PPA | Zytel® HTN |
| KumhoSunny ABS 770Z | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| OmniLon™ PA6 GR33 HS BCC12 | OMNI Plastics, LLC | Nylon 6 | OmniLon™ |