Medalist® MD-325
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Medalist® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vnL984_Medalist-MD-325.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This compound is designed for overmold to nylon. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 0.40 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 3.3 | % | ASTM D955 |
| Transverse flow | 2.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 2.14 | MPa | ASTM D412 |
| 200% strain | 3.03 | MPa | ASTM D412 |
| 300% strain | 4.00 | MPa | ASTM D412 |
| Tensile Strength (Break) | 6.21 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 600 | % | ASTM D412 |
| Tear Strength | 30.6 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 20 | % | ASTM D395 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to Nylon |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 193 - 216 | °C | |
| Middle Temperature | 260 - 282 | °C | |
| Front Temperature | 271 - 293 | °C | |
| Nozzle Temperature | 282 - 302 | °C | |
| Processing (Melt) Temp | 282 - 302 | °C | |
| Mold Temperature | 21.1 - 37.8 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.689 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| Moisture can degrade the material. Drying is suggested. This can be accomplished by placing the material in a desiccant dryer for 2 to 4 hours at 140°F. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 216 | °C | |
| Cylinder Zone 2 Temp. | 249 - 271 | °C | |
| Cylinder Zone 3 Temp. | 260 - 282 | °C | |
| Cylinder Zone 5 Temp. | 271 - 293 | °C | |
| Die Temperature | 271 - 293 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® GS8000 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Sylvin 7842-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| APEX® 3095-H | Teknor Apex Company | PVC, Flexible | APEX® |
| CERTENE™ HI-2553 | Muehlstein | HDPE | CERTENE™ |
| ESPOLEX 907 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |