Generic ABS+PBT - Glass Fiber
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vmxdPs_Generic-ABS-PBT---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+PBT - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.23 - 1.55 | g/cm³ | ASTM D792 |
| 23°C | 1.28 - 1.61 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 14 - 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.20 - 0.67 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.12 - 0.15 | % | ASTM D570 |
| 23°C, 24 hr | 0.15 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 114 - 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 67.1 - 123 | MPa | ASTM D638 |
| Yield, 23°C | 78.8 - 120 | MPa | ISO 527-2 |
| Fracture, 23°C | 77.5 - 112 | MPa | ASTM D638 |
| 23°C | 77.7 - 105 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture, 23°C | 1.5 - 4.4 | % | ASTM D638 |
| Fracture, 23°C | 2.5 - 3.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3180 - 10300 | MPa | ASTM D790 |
| 23°C | 3800 - 9770 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 86.1 - 190 | MPa | ASTM D790 |
| 23°C | 114 - 171 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.9 - 8.2 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 56 - 83 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 198 - 211 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 196 - 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 104 - 202 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 104 - 191 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 - 218 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 2.8E-5 - 6.6E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.0E-5 - 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.9E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 59.0 - 140 | °C | UL 746 |
| RTI Imp | 58.8 - 100 | °C | UL 746 |
| RTI | 60.0 - 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | |||
| 23°C | 1.0E+15 - 1.0E+17 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+15 - 2.5E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C) | 18 - 35 | kV/mm | ASTM D149 |
| Arc Resistance | 69.0 - 85.5 | sec | ASTM D495 |
| Comparative Tracking Index | 210 - 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | 19.0 - 113 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | 1.20 - 188 | mm/min | UL 746 |
| Hot-wire Ignition (HWI) | 13 - 51 | sec | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 111 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 210 - 255 | °C | |
| Middle Temperature | 230 - 255 | °C | |
| Front Temperature | 245 - 255 | °C | |
| Nozzle Temperature | 240 - 265 | °C | |
| Processing (Melt) Temp | 250 - 260 | °C | |
| Mold Temperature | 69.0 - 70.0 | °C | |
| Injection Pressure | 70.0 - 88.4 | MPa | |
| Back Pressure | 0.150 - 12.5 | MPa | |
| Screw Speed | 54 - 125 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS+PBT - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP03PET | Southern Polymer, Inc. | PET | PRIMALENE |
| Geon™ Vinyl Flexible R9788A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hanwha Total PP FB72 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| KYOCERA TCG5910 | KYOCERA Chemical Corporation | TS, Unspecified | KYOCERA |
| Karina RED COLOR CONCENTRATE 42/183-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |