Order Products : sales@su-jiao.com
XYLEX™ X8300 resin
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | XYLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vmaqMe_XYLEXX8300resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC+Polyester, UV Stabilized, Transparent |
| General Information | |
|---|---|
| Additive |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| -- | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.50 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.050 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 10 sec) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1520 | MPa | ASTM D638 |
| -- | 1600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 47.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 46.0 | MPa | ASTM D638 |
| Fracture | 54.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | > 5.0 | % | ISO 527-2/50 |
| Fracture 5 | 150 | % | ASTM D638 |
| Fracture | > 200 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 1680 | MPa | ASTM D790 |
| -- 7 | 1700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 78.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 71.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 73 | J/m | ASTM D256 |
| 23°C | 1100 | J/m | ASTM D256 |
| -30°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| -10°C 11 | 5.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 8.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 95.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 79.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 13 | 80.0 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 14 | 78.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 91.0 | °C | ASTM D1525 15 |
| -- | 96.0 | °C | ISO 306/B120 |
| Ball Pressure Test 16(85°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flow : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.23 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 750 | °C | IEC 60695-2-12 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.539 | ISO 489 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 76.7 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 249 | °C | |
| Middle Temperature | 238 - 260 | °C | |
| Front Temperature | 243 - 266 | °C | |
| Nozzle Temperature | 243 - 266 | °C | |
| Processing (Melt) Temp | 243 - 266 | °C | |
| Mold Temperature | 43.3 - 60.0 | °C | |
| Back Pressure | 0.172 - 0.517 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 120*10*4 mm |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| 16 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 230 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| ALTECH® NXT PP-H A 2040/458 GF40 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® NXT PP-H |
| Delta ABR-1G60/1 | Delta Polymers | ABS | Delta |
| HiFill® TPX-HTN-03002 A | Techmer Engineered Solutions | Nylon, Unspecified | HiFill® |
| Sylvin 5132-86 Clear Yellow 4174 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |