LNP™ LUBRICOMP™ IBI16 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vm2cYi_LNP-LUBRICOMP-IBI16-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* IBI16 is a compound based on Nylon 6/12 resin containing 30% Glass Bead, 2% Silicone. Added features of this material include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound IBL-4416 Product reorder name: IBI16 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.7 | % | |
| Across Flow : 24 hr | 1.7 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.25 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3310 | MPa | ASTM D638 |
| -- | 3300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 54.7 | MPa | ASTM D638 |
| Break | 47.9 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 83.9 | MPa | ASTM D790 |
| -- | 84.6 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 21 | J/m | ASTM D256 |
| 23°C 2 | 3.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 250 | J/m | ASTM D4812 |
| 23°C 3 | 17 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.80 | J | ASTM D3763 |
| -- | 0.970 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 169 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 76.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 79.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene P100-00 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Sup-tech A707GH | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| KOCETAL® K300FC | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| LEXAN™ XHT3141 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| BioBatch 1851 | TechnoCompound GmbH | Biodeg Polymers | BioBatch |