VAMPSTAT N 10G 09 V0 26 MF
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPSTAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vlo1cL_VAMPSTAT-N-10G-09-V0-26-MF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6 10% glass fiber reinforced, UL 94 V0 at 1,6 mm, with red phosphorus, surface resistivity 109 ohm. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | |
| Across Flow | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 20 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | °C | ASTM D648A |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 | °C | |
| Mold Temperature | 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemiton GBC0NA 70R | Franplast S.r.l. | SEEPS | Chemiton |
| Duratuf™ 903 | Technical Polymers, LLC | Acetal (POM) Homopolymer | Duratuf™ |
| Jampilen HP501D | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| LONGLITE® PMC T 359J | CCP Group | Phenolic | LONGLITE® PMC |
| PENTAMID AHT GV30 H MOS non-colored | PENTAC Polymer GmbH | Nylon 46 | PENTAMID AHT |