Order Products : sales@su-jiao.com
Ratron® 250G6-WR
| Category: | PESU , Polyethersulfone |
| Manufacturer: | Asia International Enterprise (Hong Kong) Limited |
| Trademark: | Ratron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vlLOEQ_Ratron-250G6-WR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyethersulfone (PES) is a amorphous high heat resistance engineering polymer. It is transparency, outstanding hydrolysis resistance, inherent flame retardancy, excellent resistance to a broad range of chemicals and low smoke, can withstand high temperatures under load, and provides stable performances under extreme temperature changes. This overall outstanding performance material can be used in electronic/electrical, food and tableware, military, automotive, aerospace, and medical fields. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.40 | % | |
| Flow | 0.20 | % | |
| Water Absorption (Saturation, 23°C) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 110 | MPa | ISO 527-2/1270 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 8200 | MPa | ISO 178 |
| Flexural Stress 2 | 175 | MPa | ISO 178 |
| Coefficient of Friction | 0.18 | ISO 8295 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 9.3 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | 52 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 221 | °C | ISO 306/B50 |
| CLTE - Flow (-20 to 150°C) | 2.8E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.31 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (in Oil) | 15 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 4.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4085U | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| VESTAMID® D DX9302 | Evonik Industries AG | Nylon 612 | VESTAMID® D |
| TRIMMA® SD6350H | Samyang Corporation | Acrylic (PMMA) | TRIMMA® |
| SHINSTRA WST80N | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |
| Complet® LCF20-LGF30-PA66 | PlastiComp, Inc. | Nylon 66 | Complet® |