GLAMIDE® T-521
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vlDzmm_GLAMIDE-T-521.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE®T-521 is a polyamide 6 (nylon 6) product, which contains 30% glass and mineral. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.37 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 15 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.20 - 0.40 | -- | % | ASTM D955 |
| 3.00 mm | 0.40 - 0.70 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.1 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 2.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 158 | 135 | MPa | ASTM D638 |
| Yield, 23°C | 132 | 77.0 | MPa | ASTM D638 |
| Yield, 80°C | 56.0 | 42.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.8 | 5.8 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 8400 | 7200 | MPa | ASTM D790 |
| 23°C | 6700 | 3800 | MPa | ASTM D790 |
| 80°C | 3100 | 2800 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 245 | 130 | MPa | ASTM D790 |
| Yield, 23°C | 180 | 105 | MPa | ASTM D790 |
| Yield, 80°C | 120 | 70.0 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 125 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 40 | 70 | J/m | ASTM D256 |
| 23°C | 65 | 190 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 217 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 190 | -- | °C | ASTM D648 |
| CLTE - Flow | 2.4E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 26 | 20 | kV/mm | ASTM D149 |
| Arc Resistance | 120 | 100 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Comparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-1472A | Teknor Apex Company | TPE | Telcar® |
| TOTAL Polyethylene HDPE 2285 | TOTAL Refining & Chemicals | HDPE, HMW | TOTAL Polyethylene |
| Ad-Tech Epoxy ES-204 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Cheng Yu N6C1 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| DAI-EL™ G-802 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |