FORMULA P COMP 3240
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vkqIWQ_FORMULA-P-COMP-3240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene, with 40% Talc reinforced. This material has a good stiffness and heat resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 - 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 24.0 | MPa | ISO 527-2 |
| Fracture | 17.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 20 | % | ISO 527-2 |
| Flexural Modulus | 4200 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 53.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 2.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 24 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermoset Plastics DC-441 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| AKROMID® B3 black (2502) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| DAULEN PPH GF 30 | Daunia Trading srl | PP Homopolymer | DAULEN |
| PLUSTEK PB841 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |
| Kinta FR5500-001 | Kinta Technology (Hong Kong) Co., Ltd. | PC+ABS | Kinta |