AKROMID® A3 GF 55 black (2654)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vkINgz_AKROMID-A3-GF-55-black-2654-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 55 black (2654) is a 55% glass fibre reinforced polyamide 6.6 with very high rigidity and strength Applications are mainly components in mechanical engineering and in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.40 | % | |
| Humidity Absorption - 62% RH (70°C) | 1.3 | % | ISO 1110 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break 1 | 3.5 | % | ISO 178 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 55 | % | ISO 1172 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 250 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 19000 | MPa | ISO 178 |
| Flexural Stress 3 | 410 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 18 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 100 | kJ/m² | |
| 23°C | 110 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 260 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 210 | °C | ISO 75-2/C |
| Melting Temperature 4 | 262 | °C | DIN EN 11357-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SCR21-1090 | Spartech Polycom | PBT | Spartech |
| Fainplast PVC ARC 20 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| HANWHA CP-430 | Hanwha Chemical | PVC Copolymer | HANWHA |
| KumhoSunny PC/ABS HAC8250NH-DF30 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| LNP™ LUBRICOMP™ WI001 compound | SABIC Innovative Plastics Europe | PBT | LNP™ LUBRICOMP™ |