Pebax® MV 1074 SA 01 MED

Category:	PEBA-Ether , Polyether Block Amide
Manufacturer:	Arkema
Trademark:	Pebax®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	virxrK_Pebax-MV-1074-SA-01-MED.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polyether block amide Pebax® MV 1074 SA 01 MED is a thermoplastic elastomer made of flexible and hydrophilic polyether and rigid polyamide.

Hydrophilic Pebax® MV 1074 SA 01 MED is suitable for extrusion or coextrusion and offers excellent high moisture absorption properties in wet environments, enhancing lubricity against bodily tissue.

Pebax® MV 1074 SA 01 MED is also an inherently dissipative polymer and can be dry blended or compounded with a polymer matrix to lower the surface resistivity of the final part.

This grade offers the highest quality and it is specially designed to meet the stringent requirements of the medical applications such as minimally invasive devices. Upon request, letters regarding USP Class VI compliance can be provided.

General Information
Features	Machinable
Uses	Blending Compounding Medical/Healthcare Applications Membranes Plastics Modification Tubing
Processing Method	Coextrusion Extrusion

Physical	Nominal Value	Unit	Test Method
Density	1.07	g/cm³	ISO 1183
Water Absorption			ISO 62
23°C, 24 hr	48	%
Equilibrium, 23°C, 50% RH	1.4	%

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	40		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break)	30.0	MPa	ASTM D638
Tensile Elongation (Break)	> 700	%	ASTM D638
Flexural Modulus	80.0	MPa	ISO 178

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	158	°C	ISO 11357-3

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	3.0E+9	ohms	IEC 60093
Volume Resistivity	2.5E+9	ohms·cm	IEC 60093
Charge Decay Time	< 1.0	sec	MIL B-81705

Optical	Nominal Value		Test Method
Refractive Index	1.502		Internal Method

Injection	Nominal Value	Unit
Drying Temperature	65.0 to 75.0	°C
Drying Time	4.0 to 6.0	hr
Processing (Melt) Temp	200 to 270	°C
Mold Temperature	25.0 to 60.0	°C

Extrusion	Nominal Value	Unit
Drying Temperature	65.0 to 75.0	°C
Drying Time	4.0 to 6.0	hr
Melt Temperature	210 to 230	°C

Resin Grade	Manufacturer	Category	Trademark
SHIN-A SEN-300A75	SHIN-A T&C	Epoxy	SHIN-A
Telcar® TL-85-J968-A	Teknor Apex Company	TPE	Telcar®
XANTAR® C MC 3433	Mitsubishi Engineering-Plastics Corp	PC+ABS	XANTAR® C
UNITIKA Nylon 66 A125	UNITIKA Plastics Division	Nylon 66	UNITIKA Nylon 66
GETILAN GPE/400 G	Crosspolimeri S.p.A.	XLPE	GETILAN