TOTAL Polyethylene Lumicene® M 4040
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vhsR66_TOTAL-Polyethylene-Lumicene-M-4040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M 4040 is a second generation metallocene based Polyethylene with hexene as comonomer. Lumicene® mPE M 4040 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The high stiffness combined with excellent optical properties brings a significant down-gauging potential. Lumicene® mPE M 4040 is a versatile resin that can be used in pure or in blend for the production of both monolayer and multilayer film. Main applications are: specialty film, hygiene film, embossed film, compounds and consumer and automatic packaging, such as produce bags, mailing and hygiene overwrap film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, Cast Film | 14.5 | MPa | |
| TD : Yield, 20 µm, Cast Film | 14.7 | MPa | |
| MD : Break, 20 µm, Cast Film | 33.0 | MPa | |
| TD : Break, 20 µm, Cast Film | 26.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 20 µm, Cast Film | 480 | % | |
| TD : Break, 20 µm, Cast Film | 610 | % | |
| Dart Drop Impact (20 µm, Cast Film) | 30 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | ISO 6383-2 | ||
| MD : 20.0 µm | 11.0 | kN/m | |
| TD : 20.0 µm | 90.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 122 | °C | ISO 306 |
| Melting Temperature | 126 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 20.0 µm, Cast Film) | 86 | ASTM D2457 | |
| Haze (20.0 µm, Cast Film) | 5.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 to 280 | °C | |
| Take-Off Roll | 20.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP461Y | PolyMirae | PP, Unspecified | Moplen |
| APEX® 89-P334-A | Teknor Apex Company | PVC, Flexible | APEX® |
| CGPC PVC SO-30X (60 phr Plasticizer B) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Iupilon® MB2105 | Mitsubishi Engineering-Plastics Corp | PC+Polyester | Iupilon® |
| Iupilon® H-4000 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |