SABIC® LDPE PCG06
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vdB3a3_SABICLDPEPCG06.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG06 is an additive-free grade with high purity and very low migration levels. It is typically used for semi-rigid IV containers for Large Volume Parenterals (LVP) obtained by Blow Fill Seal (BFS) process. Compliance to Regulations SABIC® LDPE PCG06 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.55 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 1.0 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 290 | MPa | ISO 527-3 |
| TD | 340 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield | 13.0 | MPa | ISO 527-3 |
| TD : Yield | 14.0 | MPa | ISO 527-3 |
| MD : Fracture | 21.0 | MPa | ISO 527-3 |
| TD : Fracture | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture | > 200 | % | ISO 527-3 |
| TD : Fracture | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | 250 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking | 10 | g | Internal method |
| Re-blocking | 30 | g | Internal method |
| Tear Strength | ISO 6383-2 | ||
| MD | 45.0 | kN/m | ISO 6383-2 |
| TD | 35.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ISO 306/A |
| Melting Temperature (DSC) | 115 | °C | DIN 53765 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 70 | ASTM D2457 | |
| Haze | 6.0 | % | ASTM D1003A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zytel® 80G33HS1L BK104 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Forprene® 6NE901A80 | SO.F.TER. SPA | TPV | Forprene® |
| Sylvin 7833-80 Black 294 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| HIFOR Xtreme® SC74845 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |
| INDURE™ X225-UV DK SHADOW | LyondellBasell Industries | Polyolefin, Unspecified | INDURE™ |