Bapolene® LL200F
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Bamberger Polymers, Inc. |
| Trademark: | Bapolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vcRrHO_Bapolene-LL200F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bapolene LL200F is a general purpose LLDPE for blown film extrusion or cast film applications. This resin offers excellent tensile and toughness properties. It is available with and without slip/antiblock additives. This product meets FDA standards for food contact applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| MD | 200 | MPa | ASTM D882 |
| TD | 241 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 9.00 | MPa | ASTM D882 |
| TD : Yield | 9.80 | MPa | ASTM D882 |
| MD : Fracture | 26.9 | MPa | ASTM D882 |
| TD : Fracture | 20.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 580 | % | ASTM D882 |
| TD : Fracture | 800 | % | ASTM D882 |
| Dart Drop Impact (38 µm) | 82 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 250 | g | ASTM D1922 |
| TD : 38 µm | 620 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 20 | % | ASTM D1003 |
| Additional Information |
|---|
| Film Thickness, 2:1 blow-up ratio: 37.5µmGloss, ASTM D2457: 38%Secant Modulus, ASTM D882, MD, 0.1 mm/mm/min initial strain rate: 200 MPaSecant Modulus, ASTM D882, TD, 0.1 mm/mm/min initial strain rate: 241 MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 199 - 227 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT4900-611UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Zhongfa PP FR-38 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PP, Unspecified | Zhongfa |
| Haysite BMC 20000 | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| Jamplast JPLGABSE | Jamplast, Inc. | ABS | Jamplast |
| POLYCASA® XT | Polycasa | Acrylic (PMMA) | POLYCASA® |