Order Products : sales@su-jiao.com
FRAGOM G/478
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | FRAGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vaez4a_FRAGOM-G-478.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRAGOM G/478: flame retardant crosslinkable compound having good temperature index and oxygen index, suitable for cable sheathing and insulation. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst. We suggest our catalyst type MAC/308 PSL to use with low compression and PVC screw. Suitable also for solar cables insulation and sheath adding 5/6% of catalyst GETILAN MAC/300 S. REACTION BETWEEN GRAFTING AND CATALYST These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 Certify: BS7211EI5, VDE0207HM1, IEC332-1, BS4066 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 7.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 48 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 12.5 | MPa | IEC 60811 |
| Tensile Strain | |||
| Fracture 1 | > 50 | % | |
| Fracture | 200 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (135°C, 168 hr) | -12 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (135°C, 168 hr) | 6.0 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 2 | IEC 60811 | ||
| 250°C | 50 | % | IEC 60811 |
| Residual : 250°C | 5.0 | % | IEC 60811 |
| Temperature index | 290 | °C | IEC 60811 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Content | % | IEC 60754-1 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Corrosion - pH | > 4.40 | IEC 60754-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 35 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 80.0 - 90.0 | °C | |
| Cylinder Zone 2 Temp. | 100 - 115 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 160 | °C | |
| Cylinder Zone 5 Temp. | 170 | °C | |
| Die Temperature | 175 | °C |
| Extrusion instructions |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion in hot water at 85/90°C for two hours (up to 0,5 mm thickness) Steam treatment at 0,15 bar for 6/8 hours Ambient air crosslinking at natural temperature and moisture, after a right number of days depending on climatic conditions. |
| Note Message | |
|---|---|
| 1 . | 5/6% addition of RESTING HF 44 |
| 2 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPCARB 1026 V0 | Vamp Tech | PC | VAMPCARB |
| VAMPAMID HT 3028 V0 | Vamp Tech | PPA | VAMPAMID |
| EverGlide® MB1950WC | Polymer Dynamix | Nylon 6 | EverGlide® |
| Fainplast PVC CKL 80 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Hanwha Total PP SI81R | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |