Daplen™ EF261AI
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Daplen™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vZ59S3_Daplen-EF261AI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Daplen EF261AI is a 20 % mineral filled polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness and is easy to process. Applications Daplen EF261AI has been developed especially for the car industry to be used in automotive interior parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/21.6 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.60 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 32.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 18.0 | MPa | ISO 527-2/50 |
| Fracture | 12.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield | 5.0 | % | ISO 527-2/50 |
| Fracture | 110 | % | ISO 527-2 |
| Flexural Modulus 2 | 1800 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% strain | 23.0 | MPa | ISO 178 |
| -- | 24.0 | MPa | ISO 178 |
| Flexural Strain | 4.9 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 16 h (100°C) | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | µgC/g | VDA 277 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 4.6 | kJ/m² | ISO 179 |
| 23°C | 43 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 65 | kJ/m² | ISO 179 |
| 23°C | No Break | ISO 179 | |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 4.5 | kJ/m² | ISO 180/1A |
| 23°C | 38 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | |||
| -20°C | 42 | kJ/m² | ISO 180 |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 94.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 118 | °C | ISO 306/A50 |
| -- | 42.0 | °C | ISO 306/B50 |
| CLTE - Flow 3 | 4.9E-5 | cm/cm/°C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Hopper Temperature | 40.0 - 80.0 | °C | |
| Processing (Melt) Temp | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Back Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100-200 m/min |
| Note Message | |
|---|---|
| 1 . | disk |
| 2 . | 2.0 mm/min |
| 3 . | -30°C/80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3WGM24 BK30564 | BASF Corporation | Nylon 6 | Ultramid® |
| Geon™ Vinyl Flexible R5155A White 759 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| PENTAMID B GV15 H natur | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| Domamid XS™ 5750R60H2 | Technical Polymers, LLC | Nylon 66 Alloy | Domamid XS™ |
| Petrothene® GA652030X02 | LyondellBasell Industries | LLDPE | Petrothene® |