LNP™ THERMOCOMP™ RFZ349XC compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vYgWXi_LNPTHERMOCOMPRFZ349XCcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RFZ349XC is a compound based on Nylon 66 resin containing Glass Fiber, Milled Glass. Added features of this material include: Flame Retardant. Also known as: LNP* THERMOCOMP* Compound RF-1007 FR MG LEX Product reorder name: RFZ349XC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.40 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.2 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.39 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.43 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11000 | MPa | ASTM D638 |
| -- | 11400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 125 | MPa | ASTM D638 |
| Fracture | 85.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.3 | % | ASTM D638 |
| Fracture | 3.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 7170 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 179 | MPa | ASTM D790 |
| -- | 197 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 2 | 7.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 590 | J/m | ASTM D4812 |
| 23°C 3 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.00 | J | ASTM D3763 |
| -- | 2.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 237 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 235 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RECANYL AR13BK9521 | Jackdaw Polymers | Nylon 66 | RECANYL |
| VENELENE® FD-4048 | Poliolefinas Internacionales, C.A. (Polinter) | LDPE+LLDPE | VENELENE® |
| ASTALON™ S1000 | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| LG PMMA BA525 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| PERSTIR® N10K7000AH0 | A.D. Compound S.p.A. | PS (GPPS) | PERSTIR® |