ACRYLITE® Resist ZK-X

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vXplGG_ACRYLITE-Resist-ZK-X.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE PLUS® ZK-X impact acrylic polymer is an amorphous, impact-modified thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA).

Typical properties of ACRYLITE PLUS® impact acrylic polymers are:

high weather resistance

high light transmission

improved resistance to stress cracking

good melt flow rate

easy to color

The special properties of ACRYLITE PLUS ZK-X polymer are:

medium impact/break resistance and strength

low melt flow rate

high heat resistance

Used for injection molded parts and extruded sheet.

General Information
Additive	Impact Modifier
Features	Amorphous Good Colorability Good Flow Good Strength Good Weather Resistance High Clarity High Heat Resistance Impact Modified Medium Impact Resistance
Uses	Appliance Components Decorative Displays Household Goods Housings Lenses Lighting Applications Writing Instruments
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Extrusion Injection Molding Sheet Extrusion

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.16	g/cm³	ASTM D792
Apparent Density	0.71	g/cm³	ASTM D1895
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)	1.0	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40 to 0.70	%	ASTM D955
Water Absorption (Equilibrium)	< 0.30	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	70		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2550	MPa	ASTM D638
Tensile Strength	64.1	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	5.0	%
Break	25	%
Flexural Modulus	2410	MPa	ASTM D790
Flexural Strength	103	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
0°C, 6.35 mm	32	J/m
23°C, 6.35 mm	45	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Annealed, 6.35 mm)	93.3	°C	ASTM D648
Vicat Softening Temperature	110	°C	ASTM D1525
CLTE - Flow (0 to 100°C)	7.2E-5	cm/cm/°C	ASTM D696

Optical	Nominal Value	Unit	Test Method
Transmittance (3200 µm)	91.5	%	ASTM D1003
Haze (3200 µm)	1.0	%	ASTM D1003
Yellowness Index (3.20 mm)	0.30	YI	ASTM D1925

Resin Grade	Manufacturer	Category	Trademark
Teflon® PFA TE9725	DuPont Fluoropolymers	PFA	Teflon® PFA
Bynel® 4157	DuPont Packaging & Industrial Polymers	LLDPE	Bynel®
Cardia Compostable™ B-MT02 (Flex)	Cardia Bioplastics™	TPS+Copolyester	Cardia Compostable™
Generic Acetal (POM) Copolymer - Metal	Generic	Acetal (POM) Copolymer	Generic
Karina CLEAR PVC COMPOUND -E 75/200	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina