ALCUDIA® EBA PA-803
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® EBA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vXoo8V_ALCUDIA-EBA-PA-803.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EBA ALCUDIA® PA-803 is a copolymer suitable for blown film applications combining excellent processability and very good mechanical properties. The butyl acrylate content is 8%. It contains antiblock additives. TYPICAL APPLICATIONS
Recommended melt temperature range is 160 to 180°C. Processing characteristics of PA-803 are similar to LDPE and conventional Polyethylene extruders are recommended. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.924 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| n-Butyl Acrylate Content | 8.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 130 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Fracture, 130 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Fracture, 130 µm, blown film | 26.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 130 µm, blown film | 680 | % | ISO 527-3 |
| TD : Fracture, 130 µm, blown film | 710 | % | ISO 527-3 |
| Dart Drop Impact (130 µm, Blown Film) | > 850 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 130 µm, blown film | 7.0 | N | ISO 6383-2 |
| TD : 130 µm, blown film | 8.5 | N | ISO 6383-2 |
| Additional Information |
|---|
| Data taken from 125 µm thickness film, blow up ratio 1:2.5, frost line height 50 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nordbak High Impact Wear Compound | Loctite® | Epoxy | Nordbak |
| Cheng Yu PP237G2 CC | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| Elastron® G G101.A65.N | Elastron USA, Inc. | SEBS | Elastron® G |
| SIBUR Synthetic Rubber SBS R 30-00A | SIBUR | SBS | SIBUR Synthetic Rubber |
| Sylvin 9600-55 Yellow 449 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |