| PA 66, 30 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | ||||
| -- | 1.36 | -- | g/cm³ | ASTM D792 |
| 23°C | 1.36 | -- | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | -- | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 290°C, 2.00mm 1 | 0.93 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.13 | -- | % | ISO 2577 |
| Flow direction : 290°C, 2.00mm 3 | 0.39 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.070 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 5.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 220 | 120 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ||||
| 23°C 5 | 9170 | 6200 | MPa | ASTM D638 |
| 23°C | 10000 | 6000 | MPa | ISO 527-2/1 |
| Tensile Strength | ||||
| Fracture, 23°C | 170 | 110 | MPa | ASTM D638 |
| Fracture, 23°C | 175 | 110 | MPa | ISO 527-2/5 |
| Tensile Elongation (Break, 23°C) | 3.0 | 6.0 | % | ASTM D638, ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 4.4 | 6.7 | % | ISO 527-2/50 |
| Flexural Modulus | ||||
| 23°C | 8690 | 6000 | MPa | ASTM D790 |
| 23°C 6 | 9200 | 5700 | MPa | ISO 178/A |
| Flexural Strength | ||||
| 23°C | 270 | 170 | MPa | ASTM D790 |
| 3.5% strain, 23°C | 265 | 150 | MPa | ISO 178/A |
| 23°C 7 | 270 | 180 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 8(23°C) | 4.0 | 6.0 | % | ISO 178/A |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behavior 9(> 1.00 mm) | passed | -- | ISO 3795 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GHR, 14-100, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| -30°C | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 60 | kJ/m² | ISO 179/1eU |
| 23°C | 75 | 85 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| -40°C, 3.18 mm | -- | 150 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 120 | -- | J/m | ASTM D256 |
| -40°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| -30°C | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 55 | -- | kJ/m² | ISO 180/1U |
| 23°C | 60 | -- | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 2.30 | -- | J | ISO 6603-2 |
| 23°C | 2.80 | 5.40 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 800 | -- | N | ISO 6603-2 |
| 23°C | 900 | 1160 | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, unannealed, 39.9mm | > 249 | -- | °C | ASTM D648 |
| 0.45 MPa, not annealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | > 240 | -- | °C | ISO 75-2/A |
| 1.8 MPa, annealing, 3.99mm | > 249 | -- | °C | ASTM D648 |
| Vicat Softening Temperature | ||||
| -- | 230 | -- | °C | ISO 306/B50 |
| -- | > 230 | -- | °C | ISO 306/B120 |
| Ball Pressure Test (253°C) | Pass | -- | IEC 60695-10-2 | |
| Melting Temperature 10 | 263 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | |||
| 0.750 mm | 125 | -- | °C | UL 746 |
| 1.50 mm | 125 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.750 mm | 90.0 | -- | °C | UL 746 |
| 1.50 mm | 105 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.750 mm | 110 | -- | °C | UL 746 |
| 1.50 mm | 115 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+15 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | |||
| 23°C, 1.00 mm | 35 | 30 | kV/mm | IEC 60243-1 |
| 23°C, 3.00 mm | 30 | 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | |||
| 23°C, 50 Hz 11 | 4.00 | 4.00 | IEC 60250 | |
| 23°C, 1 MHz 12 | 4.00 | 12.0 | IEC 60250 | |
| 23°C, 100 Hz | 4.00 | 12.0 | IEC 60250 | |
| 23°C, 1 MHz | 4.00 | 4.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 50 Hz | 0.012 | 0.27 | IEC 60250 | |
| 23°C, 100 Hz | 0.012 | 0.27 | IEC 60250 | |
| 23°C, 1 MHz | 0.019 0.019 | 0.080 0.080 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 475 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | UL 94 | |
| 1.50 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 | |
| 3.00 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 700 | -- | °C | IEC 60695-2-12 |
| 1.60 mm | 700 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 700 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 13 | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 1.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 2 mm/min |
| 9 . | US-FMVSS302 |
| 10 . | 10°C/min |
| 11 . | Tinfoil Electrodes |
| 12 . | Tinfoil Electrodes |
| 13 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 GB 30 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Vipel® F701-BID-20 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Adell Polyamide AH-33 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Karina GREEN PVC COMP. -E 850-40/174-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ QCP36 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |