Next Nylon 66 Prime Series PXIM-01NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vXKMy2_Next-Nylon-66-Prime-Series-PXIM-01NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 UnFilled impact modified Natural Compound Product Applications This grade is widely used all sector of industries such as Sports and leisure applications ski component, ski and surf binding, Toy application, battery gasket, Fastners etc Benefits Good impact resistance, Fast cycle |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.10 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 1.5 | -- | % | |
| Across Flow | 1.5 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.2 | -- | % | |
| Saturation 1 | 4.9 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 85 | -- | ||
| R-Scale | 110 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 65.0 | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | > 50 | % | ASTM D638 |
| Flexural Modulus | 2100 | 1100 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | 70.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 250 J/m | No Break | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 175 | -- | °C | |
| 1.8 MPa, Unannealed | 92.0 | -- | °C | |
| Melting Temperature | 260 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® AGV 25 Black | Radici Plastics | Nylon 66 | Radilon® |
| ASTALAC™ ABS MDA80 | Marplex Australia Pty. Ltd. | ABS | ASTALAC™ |
| Axiall PVC 10870 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Kumho STE H2030 | Korea Kumho Petrochemical Co., Ltd. | Rubber | Kumho STE |
| LNP™ THERMOCOMP™ MFB82I compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ THERMOCOMP™ |