ASTALON™ S2000U
| Category: | PC , Polycarbonate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vXDy7E_ASTALON-S2000U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALON™ S2000U / S2001U / S2003U are the standard medium viscosity (medium melt flow) grades in the ASTALON™ range and are suited to general purpose injection moulding applications which require UV stabilisation (U). Offering an exceptional combination of transparency, toughness, heat resistance, flame retardancy and processability, typical applications include emergency vehicle lighting, electrical junction box covers and marine navigation lamp lenses. Note: [ Standard grade = S2000U ] / [ FDA approved = S2001U ] / [ Steam resistant = S2003U ]. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 64.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 120 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 89.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 880 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | > 85.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 153 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 138 | °C | |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.1E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant | 2.85 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total, 3000 µm) | 85.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 125 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 275 to 295 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 110 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX/NY-GP2 | Polymer Resources Ltd. | PPE+PS+Nylon | PRL |
| RTP 305 TFE 15 SI | RTP Company | PC | RTP |
| Selvol™ 09-325 Solution | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Huaxia Shenzhou DS605 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluoropolymer | Huaxia Shenzhou |
| LUVOCOM® 50-7897 VP | Lehmann & Voss & Co. | PC | LUVOCOM® |