BJB Polyurethane F-60 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vWsst3_BJB-Polyurethane-F-60-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The F-60 A/B system is a production oriented fast gel and fast de-mold material. It features a work life which allows sufficient time to vacuum de-gas and pour air-free parts. F-60 A/B can be demolded in as little as one hour depending on part size and configuration Product Highlights:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.03 | g/cm³ | |
| -- | 1.06 | g/cm³ | ASTM D792 |
| -- 2 | 1.13 | g/cm³ | |
| Specific Volume | 0.939 | cm³/g | |
| Shrinkage | 0.30 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 8.0 - 9.0 | min | |
| Work Time 3(25°C) | 6.0 - 7.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 55 - 65 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 2.15 | MPa | ASTM D412 |
| 200% strain | 3.43 | MPa | ASTM D412 |
| 300% strain | 4.30 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 4.72 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 300 | % | ASTM D412 |
| Tear Strength | 9.98 | kN/m | ASTM D624 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 50, mixing ratio by capacity: 46 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Shelf Life (25°C) | 26 | wk | |
| Thermoset Mix Viscosity | Brookfield | ||
| -14°C 4 | 850 | cP | Brookfield |
| 25°C | 930 | cP | Brookfield |
| 25°C 5 | 550 | cP | Brookfield |
| Demold Time (25°C) | 60 - 120 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Note: Reported physical properties based on elevated temperature cured test specimens.In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 160°F (71°C). |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 100g mass |
| 4 . | Part B |
| 5 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-320 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Sylvin 9067-85 NATURAL | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| AURAPENE PPUFBK35 | Aurora Manufacturing Ltd | TPO | AURAPENE |
| Sylvin 7868-80 White 1118 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SQUARE® LIM3906-40A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |