Bergadur™ PB40 G50 BK003
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergadur™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vWOFpO_Bergadur-PB40-G50-BK003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50 % glass fiber reinforced PBT compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.72 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 - 0.70 | % | ISO 294 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 120 | MPa | ISO 527 |
| Flexural Modulus 2 | 9500 | MPa | ISO 178 |
| Flexural Strength 3 | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed, 3.20 mm) | 200 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 93 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Mold Temperature | 75.0 - 95.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Epolene® C-15P | Westlake Chemical Corporation | LDPE | Epolene® |
| Karina WHITE PVC COMPOUND -E 801-10/ 43-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kazan LDPE 102-11K | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| POLYFORT® FIPP 15 GFC BM K2258 | A. Schulman Europe | PP Copolymer | POLYFORT® |
| ALTECH® PP-H B 2015/150.01 GF15 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |