TAIRIPRO B1101
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRIPRO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vV3MRA_TAIRIPRO-B1101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC PP resin B1101 meets the requirements of FDA, RoHS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 1.5 - 1.9 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 35.3 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 200 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1420 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 3.18 mm) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.35 mm) | 110 | °C | ASTM D648 |
| Extrusion instructions |
|---|
| Screw Temp 200-230°CMolding Temp 190-210°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styroflex® PM | INEOS Styrolution Group GmbH | SBC | Styroflex® |
| ACCUCOMP™ CP0407L | ACLO Compounders Inc. | PP Copolymer | ACCUCOMP™ |
| Dryflex® T60 | ELASTO | TPE | Dryflex® |
| Electrafil® PC C BK | Techmer Engineered Solutions | PC | Electrafil® |
| HANWHA CHBA-880FR | Hanwha Chemical | Polyolefin, Unspecified | HANWHA |