Susteel® GS-40
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | TOSOH Corporation |
| Trademark: | Susteel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vUhPzo_Susteel-GS-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Glass fiber reinforced / Low-flash and toughness |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.30 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | < 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 176 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2 |
| Flexural Modulus | 14700 | MPa | ISO 178 |
| Flexural Stress | 275 | MPa | ISO 178 |
| Tensile Weld Strength | 60.0 | MPa | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length | 175 | mm | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 82 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 260 | °C | ISO 75-2/A |
| Melting Temperature | 285 | °C | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 16 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.90 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 1.4E-3 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 | |
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 270 to 300 | °C | |
| Nozzle Temperature | 290 to 330 | °C | |
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 1.00 to 20.0 | MPa | |
| Screw Speed | 100 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIPLOY® PS5660 | Sumitomo Chemical Co., Ltd. | PESU | SUMIPLOY® |
| XYLEX™ X7509HP resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |
| Hetron™ F 240 TF | Ashland Performance Materials | Polyester, TS | Hetron™ |
| Plexiglas® LED 8N LD24 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| NEOFLON™ EP-620 | DAIKIN AMERICA, INC. | ETFE | NEOFLON™ |