POLYfill PP EIP2012 F
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vTvztr_POLYfill-PP-EIP2012-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral reinforced PP Extrusion grade, Low CLTE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 to 1.4 | % | |
| Flow | 1.2 to 1.4 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 20.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 1300 | MPa | ISO 178 |
| Flexural Stress | 28.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 13 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 95.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ISO 306/A50 |
| -- | 60.0 | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3593 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC M8175 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SUPREME Specialty PS SP6489 9940 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| ULTEM™ HU2210 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Hiprolon® 400 MNNHL G30 | Arkema | Nylon 1012 | Hiprolon® |