Order Products : sales@su-jiao.com
EXCELLOY EK13C8
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | EXCELLOY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vPXnAT_EXCELLOY-EK13C8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EXCELLOY EK13C8 is an Acrylonitrile Butadiene Styrene (ABS) product filled with carbon fiber. It can be processed by injection molding and is available in Asia Pacific or North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.40 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 102 | ASTM D785 | |
| R-Scale | 103 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 74.0 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4520 | MPa | ASTM D790 |
| -- | 4500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 92.0 | MPa | ASTM D790 |
| -- | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 102 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 97.0 | °C | ISO 75-2/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 190 to 260 | °C | |
| Middle Temperature | 190 to 260 | °C | |
| Front Temperature | 190 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PVC Film 826 | Teknor Apex Company | PVC, Flexible | PVC Film |
| SolVin 360NA | INOVYN | PVC, Unspecified | SolVin |
| TOYOBO PPS TS201 HS | TOYOBO America, Inc. | PPS | TOYOBO PPS |
| LNP™ LUBRICOMP™ LL003 compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |
| PENTAMID AB MA30 H schwarz | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |