Vi-Chem PVC V221-60I
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Vi-Chem PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vOlcXM_Vi-Chem-PVC-V221-60I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vi-Chem PVC V221-60I is a Polyvinyl Chloride material filled with 12% filler. It is available in North America. Typical application of Vi-Chem PVC V221-60I: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 63 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 9.40 | MPa | ASTM D412A |
| Thermal | Nominal Value | Test Method | |
|---|---|---|---|
| Cold Flexibility 2(-30°C) | No Cracks | GM 9503P |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability - SE | 46 | mm/min | FMVSS 302 |
| Fogging | 96 | % | GM 9305P |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| High Temperature Humidity Resistance | Pass | GM 9329P | |
| Volatile Loss (105°C, < 3.20 mm) | 1.20 | ASTM D1203 | |
| Xenon Arc - Delta E 3 | 0.310 | SAE J1885 |
| Note Message | |
|---|---|
| 1 . | Die C, 500 mm/min |
| 2 . | 6 mm diameter Mandrel |
| 3 . | 601.6 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 38GFRH300 | AD majoris | PBT | MALAT |
| Vinnolit® P 70 F | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| EPO-TEK® E4110-LV | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LNP™ STAT-LOY™ M3000 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-LOY™ |
| MAJORIS FFR057 - 3717 | AD majoris | PP, Unspecified | MAJORIS |