OmniCarb™ PC/ABS 1220 CTI
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniCarb™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vOfkdh_OmniCarb-PC-ABS-1220-CTI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy Flow, Cold Temperature Impact Resistant PC/ABS |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 57.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 130 | % | ASTM D638 |
| Flexural Modulus | 2350 | MPa | ASTM D790 |
| Flexural Strength | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 430 | J/m | |
| 23°C, 3.18 mm | 640 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 116 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 288 | °C | |
| Middle Temperature | 254 to 299 | °C | |
| Front Temperature | 260 to 293 | °C | |
| Nozzle Temperature | 249 to 293 | °C | |
| Processing (Melt) Temp | 260 to 302 | °C | |
| Mold Temperature | 37.8 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH™ CP0436G20M10CL | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Fusabond® N 525 | DuPont Packaging & Industrial Polymers | Ethylene Copolymer | Fusabond® |
| LEXAN™ ML2010 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Panlite® L-1225L | TEIJIN LIMITED | PC | Panlite® |
| Sylvin 8960-62 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |